Lloydrox Rockloyd MATTRESSES 
|
Lloydrox Rockloyd Lightly Resin Bonded Rockwool Mattress conforming to IS - 8183, ASTM - C553, C592 and equivalent BS-3958 part -3 is a lightly resin bonded insulating material available with or without facing. Mattresses can be faced on one side or both sides to form a firm but flexible multi-purpose insulating materials. Service temperature of Lloydrox Rockloyd Mattress is upto 7500 C.
| FIRE SAFETY |
: In Combustible IS - 3144 : 1992 |
| ACOUSTICAL PROPERTIES |
: Suitable for acoustical insulation |
| COMPATIBILITY |
: Compatible with all form of Industrial Material |
| MOISTURE |
: Water Repellent, Non Hygroscopic |
CHEMICALLY NEUTRAL, ENVIRONMENT FRIENDLY
Lloydrox Rockloyd Mattress are specially developed to use in large process pipe-work, tanks, vessels boilers and ducts to provide unrivalled combination of matchless thermal insulation, fire protection, sound attenuation, high performance and flexibility of use.
Lloydrox Rockloyd Mattresses are also suitable where high temperatures combine with vibrations or a high fire resistance is required.
TECHNICAL SPECIFICATION
| Standard Densities* |
: 100, 120 & 150 Kg/m3 |
| Service Temperature |
: up to 750°C |
| Standard Thickness** |
: 40, 50, 65, 75 mm |
| Standard Size |
: 1520 x 1220 mm
: 4000 x 750 mm |
| Facing |
One side or both side wire netting of GI / SS |
* Other Densities are manufactured on request.
** Other thickness from 20 to 100 mm in steps of 5 mm can also be offered on request.
THERMAL CONDUCTIVITY
Lloydrox Rockloyd Mattress is tested as per IS 3346 and ASTM C592 and offer LOWEST THERMAL CONDUCTIVITY TO-WEIGHT RATIO among all industrial insulation. Thermal Conductivity or k-value of our material does not exceed the values mentioned in the adjacent table given.
| Mean Temperature °C |
Bulk Density |
80 to 120 Kg/M3 |
120 to 150 Kg/M3 |
Thermal Conductivity (mW/cm°C) |
50 |
0.43 |
0.43 |
100 |
0.52 |
0.52 |
150 |
0.62 |
0.62 |
200 |
0.73 |
0.68 |
250 |
0.84 |
0.80 |
300 |
0.95 |
0.90 |
FIRE RESISTANCE
Incombustible when tested as per IS 3144 :1992. Melting point of Fibres is above
1000°C (1832°F). Lloydrox Rockloyd Mattresses is listed suitable for A-60 fire classification.
CORROSION PROTECTION
Lloydrox Rockloyd Mattress are free of impurities like halides (Chlorides and Fluorides) and sulphides.
This is due to the fact that Lloydrox Rockloyd fibres are manufactured by dry manufacturing process and its faint alkanity actually fights corrosive reactions.
It meets various critical specifications including ASTM C795 requirement specified.
Continuously new advancements for new applications being found for this extremely versatile product.
WATER & MOISTURE REPELLENT
Lloydrox Rockloyd Mattress, by virtue of their fiber surface treatment and lay pattern, having an angle of contact exceeding 90°, results in good resistance to water absorption and moisture ingress. Lloydrox Rockloyd Mattress don't promote capillary action.
SOUND ABSORPTION
Lloydrox Rockloyd Mattresses provides excellent sound absorption by virtue of its scientific fibre lay pattern, ensuring controlled dispersion of air pockets and precise air-flow resistance and confirms to the sound absorption level as per specified under BS 3638.
ADVANTAGES
|
BENEFITS
|
 |
Excellent thermal resistance |
|
Energy conservation |
|
Wide range of service temperatures |
|
Continuous service |
|
Lightweight and user friendly |
|
Reduced installation time |
|
Long service life |
|
Good water-shedding properties |
|
Non-wicking |
|
Easy handling and application capabilities |
|
Good compressive strength |
|
Solid-resilient for banding and jacketing needs |
|
Proven acoustical performance |
|
|
|
Excellent Fire Protection |
|
|
|
|